59
IGP-HWFclassic 5907M-S3
Super-durable powder coating for silk-gloss and smooth surfaces, based on highly brilliant metal interference pigments.
download PDF
Characteristics
- Silk gloss
- Smooth finish
- Melted Metal
- Super durable facade quality,
3 years Florida > 50% residual gloss - Increased scratch resistance
Material approvals
- Qualicoat Nr. P-1535, class 2
Powder properties
Particle size:
< 100 μm
Solids:
> 99 %
Density:
1.3 kg/l-1.6 kg/l
Suitability for storage:
min. 24 months at ≤ 25 °C
in an unopened original container
Color tones:
8 shades with metal interference pigments
Film properties
Tested on
Substrate:
Aluminum (AlMg1), 0.8 mm chrom-free
Film thickness:
60 μm - 80 μm
Object temperature:
180 °C, 15 min.
Appearance
Gloss level:
71-100 R’/60°
DIN EN ISO 2813 2015-02
Mechanical tests
Cross-cut adhesion test
Gt 0
DIN EN ISO 2409 2020-12
Mandrel bending test / Tape test
≤ 5 mm
DIN EN ISO 1519 2011
Impact test / Tape test
≥ 2.5 Nm
ASTM D 2794 1993
Erichsen cupping / Tape test
≥ 5 mm
DIN EN ISO 1520 2007-11
Buchholz hardness
≥ 80
DIN EN ISO 2815 2003-10
Robustness according to Martindale, residual gloss_50%
≥ 50 %
IGP AA341.62
Weathering
3 years Florida, 5° south
> 50 % residual gloss
DIN EN ISO 2810 2021-01
Xenon-arc lamps, 1000h, 90%
> 90 % residual gloss
DIN EN ISO 16474-2 2014-03
Corrosion tests
Condensation water test, 1000h
No infiltration, no blisters
DIN EN ISO 6270-2 2018-04
Acetic acid salt spray test, 1000h
No infiltration, no blisters
DIN EN ISO 9227 2017-07
Chemical tests
Mortar resistance
Easily removable after 24h with no residues.
ASTM D 3260 2001
Processing
Pre-treatment
The substrate must be free from oil, grease and oxidation products. The pretreatment depends on the type of substrate and the corrosion protection to be achieved. We recommend the following pretreatments:
Aluminium
- Chromating according to DIN EN 12487
- Pre-anodization
- Chrome-free pretreatment according to GSB International and QUALICOAT specifications
Steel
- Zinc phosphating
Galvanised steel
- Zinc phosphating
- Chrome (III) passivation
- Chromating according to DIN EN 12487
For improved corrosion protection for applications on steel / galvanised steel, the use of corrosion protection primer IGP-KORROPRIMER 10 or IGP-KORROPRIMER 60 is recommended.
The suitability of the pretreatment method used is generally to be tested by the coater in advance with appropriate test methods. The minimum requirement for aluminium substrates / galvanised steel components is to carry out a boiling water test with a subsequent cross-cut adhesion and tape test. We refer to the guidelines of the GSB International, Qualicoat and Qualisteelcoat certifications. For further information: see also our special leaflet on pre-treatment (IGP-TI 100).
Coating devices
All conventional electrostatic systems with corona charging.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
For the construction and operation of powder coating plants, the following regulations must be complied with: ATEX RL 2014/34/EU, EN 50177, DIN EN 16985.
Recommended film thickness
80 μm - 100 μm
Whenever melted metal products are coated, the application parameter settings must be made in accordance with VR 216.
In particular, the note on purging air and gun distance in the Processing section of VR 216 must be observed.
In particular, the note on purging air and gun distance in the Processing section of VR 216 must be observed.
Curing conditions
| TObject | t min | t max |
|---|---|---|
| 170 °C | 20 minutes | 30 minutes |
| 180 °C | 15 minutes | 25 minutes |
| 190 °C | 10 minutes | 20 minutes |
Application
For safe and stable processing of the products, a slightly increased total air / metering air should be used, especially when conveying by means of pump technology.
For detailed information, please refer to the information in the section "processing" in the processing guideline VR216.
For detailed information, please refer to the information in the section "processing" in the processing guideline VR216.
Reclaimability
Small amounts of recovered powder can be added to the fresh powder, automatically if possible. Important: Keep overspray to an absolute minimum. Processing instruction VR216 must be observed.
Further information
Packaging
20 kg cardboard box with inserted antistatic PE liner
Overcoating
Preliminary tests are mandatory for overcoating painted surfaces.
Printing and glueing
Preliminary tests are mandatory for printing and glueing of painted surfaces.
Protection of coated parts
Coated parts should be packed after cooling with suitable materials without plasticizers. They should be stored protected from the weather to avoid the formation of condensation and thus water spots on the coating.
Cleaning
The coated parts must be cleaned according to the directives RAL-GZ 632 or SZFF 61.01. Technical Information IGP-TI 106 must also be observed when dealing with pearl mica effects.
Paint removal and disposal
After use, coated goods should be supplied to the normal recycling process. The disposal methods for sludges or residual powders must be observed in accordance with the local official provisions whilst taking Waste Code “080201 Coating Powder Wastes” in accordance with the European Waste Catalogue into consideration.
This application-related advice is given to the best of our knowledge. However, this information is non-obligatory and does not exempt you from carrying out your own tests. Application, use and processing of these products are beyond our control and are therefore on your responsibility. Consult the Safety Data Sheet prior to use.